Preparation and Properties of Porous Mullite Base Low-Density High-Strength Proppants
-
摘要: 目前常用的树脂复合型压裂支撑剂多存在圆球度差、抗破碎能力低、树脂用量大、成本高等不足,为解决该问题,研制了多孔莫来石基复合型低密度高强度陶粒支撑剂。通过测试支撑剂用FT酚醛环氧树脂改性前后的性能,确定了制备该支撑剂的最佳树脂质量分数和树脂含量;采用压汞分析和扫描电子显微镜对该支撑剂的显气孔率、气孔孔径分布和微观形貌进行了分析,讨论了该支撑剂的增强作用机制。结果表明:树脂的质量分数为35%时,陶粒浸渍体的体积密度最大(1.18 g/cm3),树脂的充填效果最佳,显气孔率与浸渍前的陶粒相比下降了约62%,树脂与陶粒基体相互穿插构成了网络结构,使其抗破碎能力提高;当陶粒浸渍体包覆树脂含量为5%时,颗粒表面包覆的树脂层可完全封闭陶粒浸渍体,显气孔率降低至1.06%,其视密度为1.90 g/cm3,在52和69 MPa闭合压力下的破碎率分别为2.17%和2.81%,达到行业和企业标准的技术要求。Abstract: Commonly used resin compound proppant has some shortages such as poor roundness and sphericity,low crush resistance,large quantity of resin needed,high cost and so on.To solve these problems,compound low-density high-strength proppant had been developed based on porous mullite ceramisites.The optimum mass fraction and content of resin had been worked out through evaluation of the unmodified and modified proppant with FT resin.Porosity,pore size distribution and micrograph of proppant had been studied by mercury intrusion porosity and scanning electron microscopy,and the mechanism of enhancement on compound proppant was analyzed.The results showed that when resin mass fraction was 35%,the ceramisites filled effectively with resin had the highest density of 1.18 g/cm3.The open porosity decreased by 62% compared with porous ceramisites and the crush resistance improved significantly because resin and ceramisites form an interlocking network structure.Then the impregnated matrix were coated with resin (resin content 5%),the particles were surrounded completely with resin.Its porosity dropped to 1.06% with the apparent density of 1.90 g/cm3.Crush ratios were 2.17% and 2.81% under 52 and 69 MPa closing pressure,respectively,which meet the technical requirements of the industry standard and company standard.
-
Keywords:
- porous mullite /
- resin /
- ceramsite /
- fracturing proppant /
- crush ratio /
- apparent porosity /
- micrograph
-
-
[1] 温庆志,罗明良,李加娜,等.压裂支撑剂在裂缝中的沉降规律[J].油气地质与采收率,2009,16(3):100-103. Wen Qingzhi,Luo Mingliang,Li Jiana,et al.Principle of proppant settlement in fracture[J].Petroleum Geology and Recovery Efficiency,2009,16(3):100-103. [2] Myers R,Potratz J,Moody M.Field application of new lightweight proppant in Appalachian tight gas sandstones[R].SPE 91469,2004.
[3] 蒋廷学,丁云宏,李治平,等.活性水携砂指进压裂的优化设计方法[J].石油钻探技术,2010,38(3):87-91. Jiang Tingxue,Ding Yunhong,Li Zhiping,et al.Optimization and applications of active water fingering fracturing technique[J].Petroleum Drilling Techniques,2010,38(3):87-91. [4] 张伟民,刘三琴,崔彦立,等.树脂覆膜支撑剂研究进展[J].热固性树脂,2011,26(6):55-59. Zhang Weimin,Liu Sanqin,Cui Yanli,et al.Research advance of resin coated proppants[J].Thermosetting Resin,2011,26(6):55-59. [5] 海书杰.油页岩渣制备石油支撑剂的研究[D].武汉:中国地质大学材料与化学学院,2010. Hai Shujie.Preparation of petroleum proppant from oil-shale-dreg[D].Wuhan:China University of Geosciences,School of Material Science and Chemical Engineering,2010. [6] 黄勇,高书峰,周涛,等.低密度支撑剂用酚醛/环氧树脂改性复合材料的研究[J].高分子材料科学与工程,2007,23(1):199-203. Huang Yong,Gao Shufeng,Zhou Tao,et al.The study of phenolic resin/epoxy resin enwrapped and modified nutshell composite material[J].Polymer Materials Science Engineering,2007,23(1):199-203. [7] 孙虎,汪义发,曹欣,等.低密度支撑剂的制备方法及制备工艺:中国,101200632[P].2008-06-18. Sun Hu,Wang Yifa,Cao Xin,et al.Method and preparation process for low density proppants:CN,101200632.2008-06-08. [8] McDaniel R R,Geraedts J A.Low density composite proppant,filtration media,gravel packing media,and sports field media,and method for making and using same:US,6582819.2003-06-24.
[9] SY/T 5108-2006 压裂支撑剂性能指标及测试推荐方法[S]. SY/T 5108-2006 Specification and recommended testing practice for proppants used in hydraulic fracturing operations[S]. [10] Q/SH 0051-2007 压裂用陶粒支撑剂技术要求[S]. Q/SH 0051-2007 Technical requirements for ceramisite proppants used in hydraulic fracturing operations[S].
计量
- 文章访问数: 3167
- HTML全文浏览量: 78
- PDF下载量: 3961
下载: